Effect Of Curing Methods And Scrap Tyre Addition On Properties Of Mortars

Yükleniyor...
Küçük Resim

Tarih

2020

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Croatian Association of Civil Engineers

Erişim Hakkı

Özet

Mechanical, thermal conductivity, and porosity properties of scrap tyre incorporated mortars are examined experimentally in this study for various curing conditions. Cement mortars were prepared by adding 0%, 1%, 5%, 10% and 18% of scrap tyre by cement weight, and the mortars were subjected to three curing procedures for 14 weeks. The lowest thermal conductivity values were obtained on samples containing 18% of scrap tyre by water curing and wetting-drying curing as 1.09 and 1.14 W/mK, respectively. The maximum compressive strength of 61.5 MPa was obtained on a pure sample cured by wetting and drying, while the flexural strength of pure and a 1%additive incorporated samples, which were also cured by wetting-drying, amounted to 9.1 and 8.2 MPa, respectively.

Açıklama

Anahtar Kelimeler

Mortar, Scrap tyre, Curing procedure, Thermal conductivity, Compressive strength

Kaynak

WoS Q Değeri

Q4

Scopus Q Değeri

Q2

Cilt

Sayı

Künye

GRAĐEVINAR 72 (2020) 4, 311-322