Wood And Quartz Substituted Composite Material Characteristics
Yükleniyor...
Tarih
2021
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
North Carolına State Unıv Dept Wood & Paper SCI
Erişim Hakkı
Özet
Many engineering designs focus on the production of durable, ergonomic, and economical new materials. In today’s world where natural resources are rapidly decreasing, recycling waste materials is of great importance. As a result of the bending test, the sample’s return to its original dimensions shows the plastic feature of the material. It was observed that the tensile strength can be increased if the speed of the injection machine is well adjusted in the production of tensile strength testing samples. There was an increase in the screw tensile strength of the samples and the joint hardness strength. Thermogravimetric analysis (TGA) showed that the reference samples were completely crumbled around 480 °C, and it was observed that only quartz remained from the input materials. Differential scanning calorimetry (DSC) showed that the peak point in the reference sample was at the heat flow rate of 29 m/W, while it was 18 to 19 m/W in the doped groups. Melting temperature was observed in the range of 125 to 135 °C in all groups. The mechanical properties of the quartz-substituted samples increased compared to the reference sample. It was observed that the quartz and wood powder contained in the mixture worked in harmony.
Açıklama
Anahtar Kelimeler
Quartz, Wood powder, Composite material, Bending, Injection
Kaynak
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
Sayı
Künye
BioResources 16(2), 3607-3622